Material | C60E | Steel Number | 1.1221 |
---|---|---|---|
Type | So Flanges | Standard | ASME B16.9 Plate Flanges |
High Light | C60E Slip on Plate Flange,ASME B16.9 Slip on Plate Flange,1.1221 SO Flange |
Product Description
C60E Slip on /Plate Flange 1.1221 SO Flange ASME B16.9 Plate Flanges Slip on Plate Flanges
Grade : | C60E | |||||
Number: | 1.1221 | |||||
Classification: | Quality steel | |||||
Standard: |
|
Chemical composition % of steel C60E (1.1221): EN 10277-5-2008
Cr + Mo + Ni = 0.63 |
C | Si | Mn | Ni | P | S | Cr | Mo |
0.57 - 0.65 | max 0.4 | 0.6 - 0.9 | max 0.4 | max 0.03 | max 0.035 | max 0.4 | max 0.1 |
Mechanical properties of steel C60E (1.1221)
Nominal thickness (mm): | to 16 | 16 - 100 | 100 - 250 | 250 - 500 | 500 - 1000 |
Rm - Tensile strength (MPa) (+N) | 710 | 670 | 650 | 630 | 620 |
Nominal thickness (mm): | 0.3 - 3 |
Rm - Tensile strength (MPa) (+A) | 620 |
Nominal thickness (mm): | 0.3 - 3 |
Rm - Tensile strength (MPa) (+QT) | 1150-1750 |
Nominal thickness (mm): | 5 - 10 | 10 - 16 | 16 - 40 |
Rm - Tensile strength (MPa) (+C) | 800-1150 | 780-1130 | 730-1100 |
Nominal thickness (mm): | to 8 | 8 - 20 | 20 - 50 | 50 - 80 |
Rm - Tensile strength (MPa) (+QT) | 850 | 800 | 750 | 710 |
Nominal thickness (mm): | to 8 | 8 - 20 | 20 - 50 | 50 - 80 |
ReH - Minimum yield strength (MPa) (+QT) | 580 | 520 | 450 | 420 |
Nominal thickness(mm): | to 16 | 16 - 100 | 100 - 250 | 250 - 500 | 500 - 1000 |
Re - Upper yield strength or Rp0.2 - 0.2% proof strength (MPa) (+N) |
380-390 | 340-350 | 310 | 275 | 260 |
Nominal thickness(mm): | 0.3 - 3 |
Rp0.2 0.2% proof strength (MPa) (+A) | 495 |
Nominal thickness(mm): | 5 - 10 | 10 - 16 | 16 - 40 |
Rp0.2 0.2% proof strength (MPa) (+C) | 630 | 550 | 480 |
Nominal thickness (mm): | 0.3 - 3 |
A - Min. elongation Lo = 80 mm (%) (+A) | 17 |
Nominal thickness (mm): | 5 - 10 | 10 - 16 | 16 - 40 |
A - Min. elongation at fracture (%) (+C) | 5 | 5 | 6 |
Nominal thickness (mm): | to 8 | 8 - 20 | 20 - 50 | 50 - 80 |
A - Min. elongation at fracture (%) longitud., (+QT) | 11 | 13 | 14 | 14 |
Nominal thickness (mm): | to 16 | 16 - 100 | 100 - 250 |
A - Min. elongation Lo = 5,65 √ So (%) (+N) | 10 | 11 | 11 |
Brinell hardness (HBW): (+S) | 255 |
Brinell hardness (HBW): (+A) | 241 |
Brinell hardness (HBW): (+SH) | 198 - 278 |
Vickers hardness ( HV): (+A) | 195 |
Vickers hardness ( HV): (+CR) | 305 |
Vickers hardness ( HV): (+QT) | 345 - 530 |
EU EN |
Germany DIN,WNr |
Japan JIS |
France AFNOR |
England BS |
Italy UNI |
Spain UNE |
China GB |
Russia GOST |
Inter ISO |
|||||||||||